WindForm XT

WindForm XT is a nylon and carbon material with superior mechanical properties. It is ideally suited for parts where very high performance is required such as in wind tunnel testing or on the racetrack.

Technical Data

Click here for supplier's data sheet.

General Properties Value Test
Specific Density 1.101 g/cm3  
Surface Finish – after SLS process 6.0 Ra µm  
Surface Finish – after finishing 1.8 Ra µm  
Mechanical Properties Value Test
Tensile Strength 77.78 MPa UNI EN ISO 527-1(97)
UNI EN ISO 527-2(97)
Tensile Modulus 7320.8 MPa UNI EN ISO 527-1(97)
UNI EN ISO 527-2(97)
Elongation at Break 2.6%  
Flexural Strength 131.52 MPa UNI EN ISO 14125:(2000)
Flexural Modulus 4248.5 MPa UNI EN ISO 14125:(2000)
Impact Strength (Charpy, unnotched, 23°C) 32.4 KJ/m2 ASTM D256
UNI EN ISO 179:1998
Impact Strength (Charpy, notched, 23°C) 4.73 KJ/m2 ASTM D256
UNI EN ISO 179:1998
Impact Strength (Charpy, notched, 30 °C) 4.66 KJ/m2 ASTM D256
UNI EN ISO 179:1998
Thermal Properties Value Test
Melting Point 179.33°C ASTM D3418
Heat Deflection Temperature (HDT) 175.4°C @ 1.82 MPa ASTM648
Vicat 10N 178.1°C ASTM D 1252
Data was generated from parts produced with the WindForm XT material under optimum processing conditions.

 